For repair of dies in forging industry
UTS: 95-110 kgf/mm2
YS: 80-100 kgf/mm2
Hardness as welded: 26-36 HRC
Forging dies for filling all types of die impressions. Machinery parts made of high tensile steel material in earth moving equipment. Automotive parts and certain grades of armour steel, steam turbine rotors in service up to 540oC. Repair of case hardening steel parts after removing the hard zone for repairing cracks in Ni-Cr hot working dies.
Electrode for welding Inconel 600 and similar nickel base, composition alloys
UTS: 62-78 kgf/mm2
Impact strength at +20o C 100 J at -196oC: 80 J
Basic Flux coated nickel base electrode for welding Inconel 600, inconel, incoloy monel, nickelchromium- iron alloys, HK alloys, stainless and heat resisting steels. Also for welding dissimilar metals such as carbon steels, stainless steels, nickel and nickel alloys to each other. For use on equipment and components made of pure nickel for fabrication of corrosion resistant tanks and containers, heat exchangers, furnace components, fittings, etc. Highly suitable for a wide range of dissimilar joint combinations between nickel base alloys and low alloy steels.
Electrode for welding high strength nodular cast iron
UTS: 32-43 kgf/mm2
Hardness 15-20 HRC
Electrode has easy and intimate fusion behavior with all types of cast irons. Hence best suited for welding and repairing all cast iron components, pump casings, valve flanges, foundry defects, correcting machining errors on castings and joining cast iron to steel.
Electrode for welding corrosion resistant duplex stainless steels
UTS: 70-84 kgf/mm2
For welding wrought, forged or cast duplex stainless steels for service in the as-welded condition. Offshore, oil/gas, chemical and petrochemical process industries e.g. pipe line systems, flow lines, risers, manifolds, etc.